High Performance Polyester Powder Coating MT-OA010G White

High Performance Polyester Powder Coating MT-OA010G White About

Product Description

MT-OA010G is a polyester based powder coating, formulated without TGIC.

Powder Properties

Chemical type	Polyester TGIC-free
Appearance	Smooth Gloss
Particle Size	Suitable for electrostatic spray
Specific gravity	1.54-1.64 g/cm
Film Thickness	75 100 microns
Coverage	7.8 /kg @ 75 microns
Storage	Dry cool conditions below 25C (open boxes must be resealed)
Shelf life	12 months
Stoving schedule (object temperature)	10 minutes @ 200C

Test Conditions

The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.

Substrate	Cold Rolled Steel
Pretreatment	Lightweight Zinc phosphate
Film Thickness	70 80 microns
Stoving Schedule	10 minutes at 200C

Mechanical Tests

	test	results
Flexibility	ISO6860	5mm
Erichsen cupping	ISO1520	6mm
Adhesion	ISO2409	100%
Impact (dir/rev)	ISO 6272	30/30 kgcm
Gloss(@60	ISO 2813	>90
Hardness(Buchholz)	ISO2815	>80
Reflectance Class	DIN EN 16268	A

Pre-treatment

Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA010G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.

Application

MT-OA010G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.

Superior Protection and Durability

This polyester powder coating offers high resistance to corrosion, UV rays, and weathering, making it ideal for demanding industrial environments. Its strong adhesion to properly prepared metal surfaces ensures a robust and long-lasting finish that resists chipping, fading, and peeling over time.


Eco-Conscious and Safe Formulation

MT-OA010G White contains no volatile organic compounds (VOCs) or heavy metals, ensuring safety for users and the environment. The powder form reduces waste and emissions, aligning with modern eco-friendly manufacturing practices.


Easy Application and Consistent Finish

Applied using electrostatic spray equipment, this coating delivers a smooth, uniform finish in 60-80 microns film thickness. The Standard curing schedule-180C for 10 minutes-ensures reliable and repeatable results, making it suitable for high-volume industrial operations.